Amino Moulding Compound Granular | For Electrical Components | Annual Export 1,300+ MT

No

Item

Method

Unit

Specification

Batch No. 2409211

1

Appearance

Enterprise

WHITE

WHITE

2

Flow

LASSIG

mm

190-210

205

3

Volatile Content

Enterprise

%

≤ 4.0

1.68

4

Mould Shirinkage Cold Powder

ISO 2577-1973

%

1.0 Max.

0.76

5

Preheated Powder

ISO 2577-1973

%

1.0 Max.

0.73

6

Post Shirinkage Cold Powder

ISO 2577-1973

%

-

0.45

7

Preheated Powder

ISO 2577-1973

%

-

0.42

8

Water Absorption (30 min at 100 ℃)

ISO 62-1980 (4)

mg

-

285

9

24 h at 23 ℃

ISO 62-1980 (1)

mg

150

53

10

96 h at 23 ℃

DIN 53472

mg

-

168

11

Temperature of Delfection under Load

ISO 75-1993 (E)

℃

110 Min.

133

12

Martens Temperature

DIN 43458

℃

-

120

13

Flammmability

UL94

Grade

-

V0 (3 mm)

14

Oxygen Index

ISO 4589-1984 (A)

%

-

33

15

Incandescence Resistance

DIN 53459

Grade

-

2a

16

Buring Time

ISO 181-1981

s

-

<1

17

Distance Burned

ISO 181-1981

mm

-

4.6

Mechanical Properities

18

Flexural Stress at Rupure

ISO 178-1993

MPa

80 Min.

98

19

Impact Strength-notched

ISO 178-1982

KJ/m²

1.5 Min.

2.1

20

Un-notched

ISO 178-1982

KJ/m²

6.5 Min.

8.5

Electrical Properities

21

Electrical Strength-Cold Powder

IEC 243

MV/m

5.0 Min.

7.8

22

Electrical Strength-Preheated Powder

IEC 243

MV/m

5.0 Min.

9.0

23

Insulation Resistance -24h in water

IEC 167

Ohm

10¹⁰

10¹¹

24

Tracking Resistance at 1000 V

IEC 167

V

500 Min.

> 600

25

Surface Resistance at 1000 V

DIN 53482

Ohm

10¹¹

26

Volume Resistance at 1000 V

DIN 53482

Ohm cm

10¹²

27

Dielectric DissipationFactor

DIN 53482

-

-

0.025